Injection Grade PVDF FL2008 ,Suspension, fluoropolymer PVDF resin, PVDF raw material, for valve, lining, PV film

Brand Name : Zheflon
Model Number : FL2008
Certification : reach
Place of Origin : CHINA
MOQ : 500kgs
Supply Ability : 3000Tons/Year
Delivery Time : 7~10days
Packaging Details : 25KGS/PE bag, then put into pallet
Features : homopolymer, low viscosity
Uses : Valve, lining, photovoltaic film
Forms : Translucent white particles
MFR : 15~25
Contact Now

Zheflon®FL2008 PVDF homopolymer is low viscosity grade that with high purity. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of injection.

FeaturesHomopolymer,low viscosity
UsesValve, lining, photovoltaic film
FormsTranslucent white particles
ItemsTypical Value FL2008Test Method
Physical Properties
Density(g/cc)1.77~1.79ASTM D792
Melt Flow Rate(g/10min)15.0~25.0Load 5kg,230℃,ASTM D1238
Melt viscosity(Kps)6~9

Shear Rate 100 1/s,ASTM D3835

Water Absorption(%)(Time 24 hr)≤0.040ISO 62
Linear Mold Shrinkage(cm/cm)0.0200~0.0300
Molecular Properties
Molecular weight(Da)220,000~260,000GPC,DMF,ISO 16014
Intrinsic viscosity(dl/g)0.8~0.930℃,DMAC
Molecular weight distribution1.8-2.3GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus(Thickness2.00mm)(MPa)1800~25001.0mm/min,ASTM D638
Flexural Modulus(Thickness2.00mm)(MPa)1700~23002.0mm/min,ASTM D790
Yield Strength(Thickness2.00mm)(MPa)50.0~57.050mm/min,ASTM D638
Break Strength(Thickness2.00mm)(MPa)20.0~50.050mm/min,ASTM D638
Elongation at Yield(%)5.0~1050mm/min,ASTM D638
Elongation at Break(%)20~5050mm/min,ASTM D638
Hardness, Shore D(Thickness2.00mm)75~80ASTM D2240
Izod Impact, Notched(Thickness 4.00mm, 23℃)(J/m)60~160

Notched V 10 mm


Thermal Properties
Melting Point(℃)169~173ASTM D3418
Crystallization Temperature(DSC peak)(℃)134~144ASTM D3418
Glass Transition Temp, Tg(℃)-32.0ASTM E1356
Decomposition Temperature(℃)3751% wt. loss / in air
Vicat Softening Point(℃)135~145ASTM D1525
Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(℃)105~115

After annealing 150℃,16h


Electrical Properties
Surface Resistance(ohm)≥1.00E+14

Voltage<1V,After 2 min—500V


Electrical Resistivity(ohm·cm)≥1.00E+14

Intensity=10mA,After 2 min@23℃


Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)20~25ASTM D149
Dielectric constant(1kHz,23℃)7.0~10.0ASTM D150
Burning Properties
UL Flame retardant grade(0.100mm)V-0UL94
Oxygen Index(3.00mm)44%ASTM D2683
  • Process safety instructions
  • This product should be processed under 260℃ to avoid producing toxic gases.
  • PVDF has good fire resistance and smoke inhibition property. While, it will release toxic hydrogen fluoride gas and fluorocarbon compounds when meets with fire.
  • Operators should pay attention to personal protection during the processing and operating.
  • Packaging and storage

PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.

China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Injection Grade PVDF FL2008 ,Suspension, fluoropolymer PVDF resin, PVDF raw material, for valve, lining, PV film Images

Inquiry Cart 0
Send your message to this supplier
Enter your email please.
To: Zhejiang Fluorine Chemical New Material Co., Ltd
Characters Remaining: (0/3000)
Inquiry Cart 0