Zheflon® FL2608 PVDF- Injection Grade, copolymer, fluoropolymer plastic, PVDF resin

Product Categories
Zhejiang Fluorine Chemical New Material Co., Ltd
Zhejiang Fluorine Chemical New Material Co., Ltd
City: Hangzhou
Province/State: Zhejiang
Country/Region: China
Tel: 86-575-82727701

Zheflon® FL2608 PVDF- Injection Grade, copolymer, fluoropolymer plastic, PVDF resin

Brand Name : Zheflon
Model Number : FL2606
Certification : Reach
Place of Origin : China
MOQ : 500KGS
Supply Ability : 3000tons/Year
Delivery Time : 7~10 days
Packaging Details : PE bag/ Pallet
Features : Copolymer, Low viscosity
Uses : wire, cable
Forms : Translucent white particles
Contact Now

Zheflon®FL2608 PVDF copolymer is low viscosity grade, especially suitable for applications in the cable industry. It gives the cable excellent mechanical properties, flexibility and electrical performance; high temperature corrosion resistance; low flammability, smoke emission. In addition, the zero-perfluorooctanoic acid and heavy metal content to comply with RoHS requirements.

FeaturesCopolymer, Low viscosity
UsesWire, Cable
FormsTranslucent white particles
ItemsTypical Value FL2608Test Method
Physical Properties
Density(g/cc)1.77~1.80ASTM D792
Melt Flow Rate(g/10min)15.0~25.0Load 5kg,230℃,ASTM D1238
Melt viscosity(Kps)6~9

Shear Rate 100 1/s,ASTM D3835

Water Absorption(%)(Time 24 hr)≤0.040ISO 62
Linear Mold Shrinkage(cm/cm)0.0200~0.0300
Molecular Properties
Molecular weight(Da)250,000~280,000GPC,DMF,ISO 16014
Intrinsic viscosity(dl/g)0.85~1.0030℃,DMAC
Molecular weight distribution2.0-3.0GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus(Thickness2.00mm)(MPa)600~10001.0mm/min,ASTM D638
Flexural Modulus(Thickness2.00mm)(MPa)800~10002.0mm/min,ASTM D790
Yield Strength(Thickness2.00mm)(MPa)25.0~35.050mm/min,ASTM D638
Break Strength(Thickness2.00mm)(MPa)20.0~30.050mm/min,ASTM D638
Elongation at Yield(%)10.0~15.050mm/min,ASTM D638
Elongation at Break(%)200~60050mm/min,ASTM D638
Hardness, Shore D(Thickness2.00mm)70~75ASTM D2240
Izod Impact, Notched(Thickness 4.00mm, 23℃)(J/m)100~150

Notched V 10 mm


Thermal Properties
Melting Point(℃)158~166ASTM D3418
Crystallization Temperature(DSC peak)(℃)115~130ASTM D3418
Glass Transition Temp, Tg(℃)-32.0ASTM E1356
Decomposition Temperature(℃)330~3501% wt. loss / in air
Vicat Softening Point(℃)90~105ASTM D1525
Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(℃)50~60

After annealing 150℃,16h


Electrical Properties
Surface Resistance(ohm)≥1.00E+14

Voltage<1V,After 2 min—500V


Electrical Resistivity(ohm·cm)≥1.00E+14

Intensity=10mA,After 2 min@23℃


Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)20~25ASTM D149
Dielectric constant(1kHz,23℃)7.0~10.0ASTM D150
Burning Properties
UL Flame retardant grade(0.100mm)V-0UL94
Oxygen Index(3.00mm)44%ASTM D2683

Process safety instructions

  • This product should be processed under 260℃ to avoid producing toxic gases.
  • PVDF has good fire resistance and smoke inhibition property. While, it will release toxic hydrogen fluoride gas and fluorocarbon compounds when meets with fire.
  • Operators should pay attention to personal protection during the processing and operating.

Packaging and storage

PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.

China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Zheflon® FL2608 PVDF- Injection Grade, copolymer, fluoropolymer plastic, PVDF resin Images

Inquiry Cart 0
Send your message to this supplier
Enter your email please.
To: Zhejiang Fluorine Chemical New Material Co., Ltd
Characters Remaining: (0/3000)
Inquiry Cart 0